Laser/Electron Beam Processing of As-cast Nd_2Fe_(14)B Alloy

HU Jiandong , ZHANG Xujun , SHI Zhusheng Microanalysis Center , Jilin University of Technology , Changchun , 130025 , China.Department of Metallurgy and Materials , University of Birmingham U.K.

材料科学技术（英）

It was found that the free Fe in the melted zone of the as—cast Nd_2Fe_(14)B alloy could be dissolved by Iaser/electron beam.The growth direction of Nd_2Fe_(14)B grains is nearly perpendicular to the sur- face of the samples.EDX examination showed that Fe element was homogeneously distributed in the melted zone.Results presented in this paper have giv- en hint to remove free Fe in as—cast Nd_2Fe_(14)B alloy.

关键词: Nd-Fe-B alloy , null

MAGNETIC PROPERTIES OF Nd_2(Fe_(1-x)M_x)_(14)B(M=C,Si)ALLOYS

XING Feng JIANG Chao HE Wenwang Department of Physics , Peking University , Beijing , China [Originally published in ACTA METALL SIN (CHINESEEDN) 24 (5) 1988pp B348—B352 , received 22 October 1986:in revised form 8 May 1987]

金属学报(英文版)

The magnetic properties of Nd_2(Fe_(1-x)M_x)_(14)B(M=C and Si) compounds have been investi- gated.Substituting Fe by small amount of metalloid C and Si atoms,the compounds are in tetragonal structure and have uniaxial anisotropy.The substitution of C for part of Fe de- creases the Curie temperature of the compounds and the intrinsic coercivity of bond samples at low temperature.The replacement of Fe by Si makes the Curie temperature increase with a maximum at the vicinity of x=0.15.When the range of the content of Si is 0≤x≤0.10,the coercivity distinctly increases at room temperature.from 62.7 kA/m at x=0 to 138.7kA/m at x=0.06,where the residual magnetization has a maximum:in the mean time the saturation magnetization decreases only by a small amount.

关键词: Nd-Fe-B alloy , null , null

Microstructure and Coercivity in High H_c Sm(Co, Cu, Fe, Zr)_(7.4) and Nd-Fe-B Alloys

PAN Shuming , XIAO Yaofu General Research Institute of Nonferrous Metals , CNNC. Beijing , China. University of Science and Technology Beijing , China. To whom correspondence should be addressed.

材料科学技术（英）

关键词: HVEM observation , null , null

物理法整体再利用废弃Nd-Fe-B合金研究

唐杰 , 张铭杰 , 王晓军 , 赵导文 , 张林 , 魏成富

稀有金属 doi:10.13373/j.cnki.cjrm.2015.09.003

烧结Nd-Fe-B合金加工过程中会产生10％～ 30％的边角料、成型中可能的氧化粉末、烧结过程失误的废品及使用后的产品等,其中含有大量的Fe与丰富的稀土元素.一般研究主要的注意力集中在稀土元素的回收,也有部分仅针对Fe元素的回收利用研究,而对其他元素丢弃或者采用另外的方式处理,造成材料、资源的浪费,工艺成本亦相应增加.为综合利用有限资源,在(PrNd)xB1.05Al0.5Nb0.3 Fe98.15-x合金的制备过程中,采用物理手段添加一定含量的废弃Nd-Fe-B磁体,从而制备出合格产品,并与不添加废弃磁体的(PrNd)xB1.05Al0.5Nb0.3Fe98.15-x合金进行对比研究.结果表明,经X射线衍射(XRD)分析,在废料少量添加的情况下,二者的物相相似,且经50℃老化处理1h后,两种样品磁通量分别降低了0.51和0.52 Wb,经70℃处理1h后,降低了0.96和0.95 Wb,再经90℃处理1h后,又分别降低了0.80和0.82 Wb.相对于无废弃Nd-Fe-B磁体的样品,添加废料样品粉末颗粒较粗,比表面积较小,离散性稍大,但是其块体样品的微观结构基本一致.

关键词: Nd-Fe-B合金 , 废弃 , 热稳定性 , 微观结构 , 平均粒度

Succession law of Nd-Fe-B alloys with different coercivities

Jie Tang , Li-Rong Yang , Lin Zhang , Cheng-Fu Wei , Yang Mei , Yong-Ge Wen

稀有金属（英文版） doi:10.1007/s12598-014-0228-0

关键词:

采用Matlab软件分析(PrNd)xAl0.12Nb0.2Cu0.13B1.05Fe98.5-x合金的失重性能

唐杰 , 杨梨容 , 张铭杰 , 王晓军 , 赵导文 , 张林 , 魏成富 , 张兵

材料导报 doi:10.11896/j.issn.1005-023X.2014.18.023

研究了采用高压加速老化试验机对HD工艺和普通工艺制备的两种(PrNd)xAl0.12Nb0.2Cu013B1.05-Fe98.5-x合金样品在温度为130℃,压强为0.22 MPa,湿度为95％的极端环境条件下处理168 h后的失重情况,通过磁化特性自动测量仪检测了其老化前后的磁性能,用激光粒度仪测试了其原始粉末粒度,并用Matlab软件对两种样品的SEM微观结构照片中富Nd相的含量进行了分析.结果表明,两种样品的富Nd相含量有区别,普通工艺制备样品为7.63％,而HD工艺制备样品为7.80％,且磁性能也较好,粉末平均粒度较小,前者却相对较大.此外,二者的平均失重率分别是-3.5386 mg·cm-2和-0.1645 mg·cm-2.另一方面,经过失重试验后,前者的剩余磁通密度Br降低了0.74％,后者仅仅降低了0.64％,两者的内禀矫顽力Hej也分别降低了2.28％和1.14％,方形度Hk/Hb分别降低了24.9％和0.10％,最大磁能积(BH)max降低了2.84％和2.06％.

关键词: Nd-Fe-B合金 , HD工艺 , 常规工艺 , 失重 , Matlab软件

烧结Nd-Fe-B合金断裂机制和增韧方法

唐杰 , 王晓军 , 杨梨容 , 张林 , 魏成富

材料导报 doi:10.11896/j.issn.1005-023X.2016.017.014

Nd-Fe-B合金磁性能的提升扩大了其应用范围，但也存在韧性差、脆性大、抗震和抗冲击能力差的缺点，使其在机械加工过程中易开裂，降低了成品率和加工精度，提高了生产成本，也限制了其在高精度仪器仪表、高速电机等领域的应用。因而如何提高其力学性能逐渐成为研究的重点，由此需要探索清楚其断裂机制，并采用适当而有效的方法进行该合金的增韧。基于此目的，综述了近年来Nd-Fe-B合金断裂机制方面的研究成果，分析了其主要是沿晶断裂，只是缺陷的存在会增加穿晶断裂的几率。同时，指出了元素的添加和改善制备工艺是合金增韧的两条途径，不过目前并没有从根本上改变其力学性能差的缺点，所以需要在未来的研究中进一步深入，寻求更为行之有效的增韧方式。

关键词: Nd-Fe-B合金 , 力学性能 , 断裂 , 增韧方法

Nd_2(Fe_(1-x)M_x)_(14)B(M=C,Si)合金的磁性

邢峰 , 江潮 , 何文望

金属学报

本文研究了Nd_2(Fe_(1-x)M_x)_(14)B的磁性。少量类金属原子C和Si取代部分Fe,能形成四方结构,且具有单轴各向异性。碳取代Fe,使化合物的Curie温度降低,低温下粘结体样品的内禀矫顽力减少;而Si对Fe的取代可使Curie温度升高,并在x=0.15附近达到极大值。含Si样品在0≤x≤0.10范围内,矫顽力显著增加,室温下从x=0的62.7kA/m增加到x=0.06的138.7 kA/m,并且在x=0.06附近,剩磁有一个极值,饱和磁化强度减少不多。

关键词: Nd-Fe-B合金 , magnetic properties , Curie temperature